Tantalum Top Hat Single Crystal
Formula: Ta
Percentage Purity: 99.999%
Top Section Thickness: 1mm
Bottom Section Thickness: 1mm
Outside Diameter: 10mm
Inside Diameter: 8mm
Orientation: -100
Orientation Accuracy: Approx. 0.1°
Polish: Polished
Surface Finish: =< 0.03µm Ra
CAS Number: 7440-25-7
UOM Code: 779-392-54
Legacy Code: TA002033
Distributor Code: GF77939254
SKU: 1000210982
Product Code: TA00-SC-000195
Percentage Purity: 99.999%
Top Section Thickness: 1mm
Bottom Section Thickness: 1mm
Outside Diameter: 10mm
Inside Diameter: 8mm
Orientation: -100
Orientation Accuracy: Approx. 0.1°
Polish: Polished
Surface Finish: =< 0.03µm Ra
CAS Number: 7440-25-7
UOM Code: 779-392-54
Legacy Code: TA002033
Distributor Code: GF77939254
SKU: 1000210982
Product Code: TA00-SC-000195
Material Properties for Metals
Atomic Properties
| Element | Value |
|---|---|
| Atomic number | 73 |
| Crystal structure | Body centred cubic |
| Electronic structure | Xe 4f¹⁴ 5d³ 6s² |
| Valences shown | 2,3,4,5 |
| Atomic weight( amu ) | 180.9479 |
| Thermal neutron absorption cross-section( Barns ) | 22 |
| Photo-electric work function( eV ) | 4.1 |
| Natural isotope distribution( Mass No./% ) | 180/ 0.012 |
| Natural isotope distribution( Mass No./% ) | 181/ 99.988 |
| Atomic radius - Goldschmidt( nm ) | 0.147 |
| Ionisation potential( No./eV ) | 1/ 7.88 |
| Ionisation potential( No./eV ) | 2/ 16.2 |
Mechanical Properties
| Element | Value |
|---|---|
| Material condition | Hard |
| Material condition | Soft |
| Poisson's ratio | 0.342 |
| Poisson's ratio | 0.342 |
| Bulk modulus( GPa ) | 196.3 |
| Bulk modulus( GPa ) | 196.3 |
| Tensile modulus( GPa ) | 185.7 |
| Tensile modulus( GPa ) | 185.7 |
| Hardness - Vickers( kgf mm⁻² ) | 200 |
| Hardness - Vickers( kgf mm⁻² ) | 90 |
| Tensile strength( MPa ) | 760 |
| Tensile strength( MPa ) | 172-207 |
| Yield strength( MPa ) | 705 |
| Yield strength( MPa ) | 310-380 |
Electrical Properties
| Element | Value |
|---|---|
| Electrical resistivity( µOhmcm ) | 13.5@20@20°C |
| Superconductivity critical temperature( K ) | 4.47 |
| Temperature coefficient( K⁻¹ ) | 0.0035@0-100°C |
| Thermal emf against Pt (cold 0C - hot 100C)( mV ) | 0.33 |
Physical Properties
| Element | Value |
|---|---|
| Boiling point( C ) | 5425 |
| Density( gcm⁻³ ) | 16.6@20°C |
Thermal Properties
| Element | Value |
|---|---|
| Melting point( C ) | 2996 |
| Latent heat of evaporation( J g⁻¹ ) | 4165 |
| Latent heat of fusion( J g⁻¹ ) | 174 |
| Specific heat( J K⁻¹ kg⁻¹ ) | 140@25°C |
| Thermal conductivity( W m⁻¹ K⁻¹ ) | 57.5@0-100 |
| Coefficient of thermal expansion( x10⁻⁶ K⁻¹ ) | 6.5@0-100°C |