VICTREX® APTIV® 1102 20% mineral filled PEEK Coil - T 0.125mm W 610mm L 1.5m
Grade: VICTREX® APTIV® 1102
Formula: PEEK
Thickness: 0.125mm
Coil Width: 610mm
Length: 1.5m
Structure: Semi Crystalline
Surface Finish: Matt/Matt
Colour: Grey
UOM Code: 642-321-19
Legacy Code: EK361125
Distributor Code: GF64232119
SKU: 1000111618
Product Code: EK36-FM-000125
Formula: PEEK
Thickness: 0.125mm
Coil Width: 610mm
Length: 1.5m
Structure: Semi Crystalline
Surface Finish: Matt/Matt
Colour: Grey
UOM Code: 642-321-19
Legacy Code: EK361125
Distributor Code: GF64232119
SKU: 1000111618
Product Code: EK36-FM-000125
Material Properties for Polymers
Chemical Resistance
| Element | Value |
|---|---|
| Acids - concentrated | Good-Poor |
| Acids - dilute | Good |
| Alcohols | Good |
| Alkalis | Good |
| Aromatic hydrocarbons | Good |
| Greases and Oils | Good |
| Halogenated Hydrocarbons | Good |
| Halogens | Good-Poor |
| Ketones | Good-Poor |
Physical Properties
| Element | Value |
|---|---|
| Radiation resistance | Good |
| Density( gcm⁻³ ) | 1.45 |
Mechanical Properties
| Element | Value |
|---|---|
| Elongation at break( % ) | >10 (TD) - 7 (TD) |
| Elongation at break( % ) | >100 (MD) - 6 (MD) |
| Elongation at break( % ) | 10(TD) |
| Elongation at break( % ) | 100(MD) |
| Tensile modulus( GPa ) | 4.5-5(MD) |
| Tensile modulus( GPa ) | 4.2-4.5 (TD) - |
| Tensile modulus( GPa ) | 4.2-4.5(TD) |
| Tensile modulus( GPa ) | 4.5-5.0 (MD) - Good |
| Tensile strength( MPa ) | 80 (TD) - 4.2-4.5 (TD) |
| Tensile strength( MPa ) | 100(MD) |
| Tensile strength( MPa ) | 100 (MD) - 4.5-5.0 (MD) |
| Tensile strength( MPa ) | 80(TD) |
| Tear strength( N mm⁻¹ ) | 6(MD) |
| Tear strength( N mm⁻¹ ) | 7(TD) |
| Tear strength( N mm⁻¹ ) | 7 (TD) - |
| Tear strength( N mm⁻¹ ) | 6 (MD) - 200 |
Electrical Properties
| Element | Value |
|---|---|
| Dielectric strength( kV mm⁻¹ ) | 200 |
| Volume resistivity( Ohmcm ) | 10¹⁵ |
Thermal Properties
| Element | Value |
|---|---|
| Thermal conductivity( W m⁻¹ K⁻¹ ) | 0.43-0.91 |
| Coefficient of thermal expansion( x10⁻⁶ K⁻¹ ) | 35 |