Aluminum Disk Single Crystal
Formula: Al
Percentage Purity: 99.999%
Thickness: 2mm
Diameter: 12mm
Orientation: -110
Orientation Accuracy: Approx. 0.1°
Polish: Polished
Surface Finish: =< 0.03µm Ra
CAS Number: 7429-90-5
UOM Code: 105-171-59
SKU: 1000018332
Product Code: AL00-SC-000419
Percentage Purity: 99.999%
Thickness: 2mm
Diameter: 12mm
Orientation: -110
Orientation Accuracy: Approx. 0.1°
Polish: Polished
Surface Finish: =< 0.03µm Ra
CAS Number: 7429-90-5
UOM Code: 105-171-59
SKU: 1000018332
Product Code: AL00-SC-000419
Material Properties for Metals
Atomic Properties
| Element | Value |
|---|---|
| Atomic number | 13 |
| Crystal structure | Face centred cubic |
| Electronic structure | Ne 3s² 3p¹ |
| Valences shown | 3 |
| Atomic weight( amu ) | 26.98154 |
| Thermal neutron absorption cross-section( Barns ) | 0.232 |
| Photo-electric work function( eV ) | 4.2 |
| Atomic radius - Goldschmidt( nm ) | 0.143 |
| Ionisation potential( No./eV ) | 4/ 120 |
| Ionisation potential( No./eV ) | 5/ 154 |
| Ionisation potential( No./eV ) | 6/ 190 |
| Ionisation potential( No./eV ) | 1/ 5.99 |
| Ionisation potential( No./eV ) | 3/ 28.4 |
| Ionisation potential( No./eV ) | 2/ 18.8 |
Mechanical Properties
| Element | Value |
|---|---|
| Material condition | Soft |
| Material condition | Hard |
| Poisson's ratio | 0.345 |
| Poisson's ratio | 0.345 |
| Bulk modulus( GPa ) | 75.2 |
| Bulk modulus( GPa ) | 75.2 |
| Tensile modulus( GPa ) | 70.6 |
| Tensile modulus( GPa ) | 70.6 |
| Hardness - Vickers( kgf mm⁻² ) | 21 |
| Hardness - Vickers( kgf mm⁻² ) | 35-48 |
| Tensile strength( MPa ) | 130-195 |
| Tensile strength( MPa ) | 50-90 |
| Yield strength( MPa ) | 110-170 |
| Yield strength( MPa ) | Oct-35 |
Electrical Properties
| Element | Value |
|---|---|
| Electrical resistivity( µOhmcm ) | 2.67@20@20°C |
| Superconductivity critical temperature( K ) | 1.175 |
| Temperature coefficient( K⁻¹ ) | 0.0045@0-100°C |
| Thermal emf against Pt (cold 0C - hot 100C)( mV ) | 0.42 |
Physical Properties
| Element | Value |
|---|---|
| Boiling point( C ) | 2467 |
| Density( gcm⁻³ ) | 2.7@20°C |
Thermal Properties
| Element | Value |
|---|---|
| Melting point( C ) | 660.4 |
| Latent heat of evaporation( J g⁻¹ ) | 10800 |
| Latent heat of fusion( J g⁻¹ ) | 388 |
| Specific heat( J K⁻¹ kg⁻¹ ) | 900@25°C |
| Thermal conductivity( W m⁻¹ K⁻¹ ) | 237@0-100°C |
| Coefficient of thermal expansion( x10⁻⁶ K⁻¹ ) | 23.5@0-100°C |